We are a globally recognized trader and exporter of optimum quality Polyetheretherketone Rods that are acknowledged for their use in hot water without any permanent loss in physical properties. The offered rods are designed and manufactured by our vendors using the best grade polyetheretherketone material and advanced technology. These Polyetheretherketone Rods are available in different lengths and thicknesses as per the diverse needs of clients. Provided rods are quality tested by our vendors to eradicate any kind of flaw prior to dispatch from their end.
Features:
Material description
General properties | ||||
Density | 1.32 | g/cm3 | DIN EN ISO 1183-1 | |
Flammability | V0/V0 | 3 mm / 6 mm | UL 94 | |
Absorption of moisture | 0.20 | % | DIN EN ISO 62 | |
Mechanical properties | ||||
Yield stress/ tensile strength | 110 | MPa | DIN EN ISO 527 | |
Tensile elongation | 20 | % | DIN EN ISO 527 | |
Tensile modulus of elasticity | 4,000 | MPa | DIN EN ISO 527 | |
Notched impact strength (Charpy) | 5 | kJ/m2 | DIN EN ISO 179 | |
Ball indentation hardness | 230 | MPa | DIN EN ISO 2039-1 | |
Shore hardness | 88 | Skala D | DIN EN ISO 868 | |
Thermal properties | ||||
Melting temperature | 343 | C | ISO 11357-3 | |
Thermal conductivity | 0.25 | W / (m K) | DIN 52612-1 | |
Specific thermal capacity | 1.34 | kJ / (kgK) | DIN 52612 | |
Coefficient of linear thermal expansion | 50 | 10-6 K-1 | DIN 53752 | |
Service temperature, long term (min.) | -60 | C | Benchmark | |
Service temperature, long term (max.) | 250 | C | Benchmark | |
Service temperature, short term | 31 | C | Benchmark | |
Heat deflection temperature | 152 | C | DIN EN ISO 75 (HDT A) | |
Electrical properties | ||||
Dielectric constant | 3.20 | | DIN IEC 60250 | |
Dielectric dissipation factor | 0.001 | | DIN IEC 60250 | |
Specific volume resistivity | 4.9 1016 | cm | DIN IEC 60093 | |
Surface resistivity | 1018 | | DIN EN 60093 | |
Dielectric strength | 20 | kV/mm | DIN EN 60243 |